Loctite ® 609™ Retaining Compound, Cylindrical bonding
Loctite ® 609™ is a low viscosity, rapid-curing anaerobic adhesive that augments the strength of press fit assemblies or slip fit assemblies up to 0.005"in diameter. Adds up to 3,000 psi holding power. Recommended for parts that will need subsequent dismantling, i.e., retention of bearings onto shafts and into housings.
Typical applications: Augment press fits
Cure Time: Fixture - 10 minutes Full - 24 hours
Max gap fill: 0.12mm
Temperature resistance: 150°C
Shear strength: 15.8 /mm2
Other top picks for Retaining Compound
>Loctite ® 620™ Retaining Compound, Cylindrical bonding, High temperature
Locating pins in radiator assemblies, sleeves into pump housings and bearings in auto transmissions.
>Loctite ® 641™ Retaining Compound, Cylindrical bonding
Typical applications include retention of bearings onto shafts and into housings.
>Loctite ® 648™ Retaining Compound, Cylindrical bonding
Holding gears and sprockets onto gearbox shafts and rotors on electric motor shafts
>Loctite ® 660™ Quick Metal ® Retaining Compound, Cylindrical bonding
Restoring correct fits on worn shafts, spun bearings, and damaged keyways
>Loctite ® 680™ Retaining Compound, Cylindrical bonding
Recommended for retaining shafts, gears, pulleys, and similar cylindrical parts
>Loctite ® 638™ Retaining Compound, Cylindrical bonding
A maximum strength retaining compound for use where high dynamic force or cyclic loading is expected.
Loctite Retaining Compounds
Retaining compounds is considered to be an industry anabolic adhesive with high bond strength and cure speed, which could be used to eliminate fretting corrosion, and the need for expensive replacement parts, or time consuming machining.